cement that may irritate pulp if liner is not used
|
zinc phosphate
|
|
has exothermic properties
|
zinc phosphate
|
|
mixed on cool glass slab
|
zinc phosphate
|
|
primary consistency as luting
|
zinc phosphate
|
|
secondary consistency as base
|
zinc phosphate
|
|
brandname Flecks
|
zinc phosphate
|
|
consistency that should pull up about 1"
|
luting
|
|
cleaned w/ baking soda and water
|
zinc phosphate
|
|
brandname Durelon
|
polycarboxylate
|
|
mixes quickly and is very sticky
|
polycarboxylate
|
|
used for permanent luting under indirect restorations and cementation under orthodontic bands
|
zinc phosphate
|
|
used for final cementation of indirect restorations or high-strength base
|
polycarboxylate
|
|
brandnames ZOE, B&T, IRM, Temp-bond
|
zinc oxide eugenol
|
|
used for temp cementation, temp or intermediate restorations, high-strength bases, root canal sealer & perio dressing
|
ZOE
|
|
sedative to pulp
|
ZOE
|
|
2nd consistency serves as temp restoration or sedative base
|
ZOE
|
|
primary consistency serves as temp or rarely perm luting agent
|
ZOE
|
|
cleaned with orange oil
|
ZOE
|
|
2nd consistency may need to be stropped
|
ZOE
|
|
neutral pH of 7
|
ZOE
|
|
cannot be used under composite restorations or resin or hybrid based cements
|
ZOE
|
|
brandname Cavitec, Cavalite
|
ZOE as liner
|
|
brandname Dycal, Alkaliner
|
calcium hydroxide
|
|
used as cavity liner where dentin no longer covers pulp
|
calcium hydroxide
|
|
used as pulp-cap
|
calcium hydroxide
|
|
brandname Copal F, Capelite
|
cavity varnish
|
|
encourages growth of secondary dentin
|
calcium hydroxide
|
|
used as insulator
|
cavity varnish
|
|
2 cements w/ F release
|
glass ionomer, hybrid
|
|
insoluable cement
|
resin based cement
|
|
not recommended under ceramic
|
hybrid ionomer
|
|
can cause mild-sever post-op sensitivity
|
glass ionomer
|
|
increased tensile and copmpressive strength, decreased solubility, F release
|
hybrid ionomer
|
|
good bond strength and insolubility at margins
|
resin-based cement
|
|
3 low-strength base/liner
|
calcium hydroxide, glass ionomer, ZOE
|
|
4 high-srength base/buildup
|
reinforced ZOE, zinc phosphate, polycarboxylate, glass ionomer
|
|
permanent cementation for cast crowns
|
zinc phosphate, polycarboxylate, glass ionomer, hybrid ionomer, resin-based
|
|
porcelain, ceramic or composite veneers, inlays, onlys and crown permanent cementation
|
resin-based
|
|
permanent cementation under orthodontic bands
|
glass ionomer, zinc phosphate + F
|
|
permanent cementation under ortho brackets
|
resin-based
|
|
provisional cementation
|
ZOE
|
|
provisional restorations
|
ZOE, polycarboxylate, zinc phosphate
|
|
surgical dressing
|
ZOE
|